Polyvinyl oti (PVA) Sinopec
Awọn ọja PVA ti pin kaakiri ni awọn igbesi aye wa, ati pe a lo ni lilo pupọ ni ipara aṣọ, iwe afọwọṣe iwe, afọwọṣe rewettable, alemora oju iwe, ti ngbe pigmenti, alemora ti a bo ile, awọn ohun elo ile alemora ati awọn afikun, irugbin ati awọn aṣoju aabọ elegbogi, inorganic ati awọn ọja itanna. adhesives, awọn fiimu itusilẹ omi, awọn afikun ohun ikunra, polymerization vinyl acetate emulsion ati fainali chloride idadoro polymerization amuduro.Fiimu aabo igba diẹ, bbl Pẹlu ilọsiwaju ilọsiwaju ti imọ-ẹrọ ọja, aaye ohun elo rẹ tun ti fẹ siwaju sii.
Ifihan sipesifikesonu
PVA ni pipe awọn ọja jara alkolysis:
098-05, 098-08, 098-10, 098-15, 098-20, 098-27, 098-30, 098-39, 098-45, 098-70,02,098-705 27S, 100-35, 100-40, 100-60, 100-70, 100-78
Awọn ọja jara agbedemeji ọti-lile PVA:
092-20, 094-27, 096-27, 095-28, 097-29, 092-35, 092-53, 097-60, 097-70
PVA apa kan alcoholysis awọn ọja jara:
088-05,088-07,088-13,088-17,088-20,080-22,088-26,088-35,080-44,088-50,088-60
Awọn paramita alaye
Atọka PVA Sinopec Ṣe imuse boṣewa orilẹ-ede (gb/t 12010.3-2010) | ||||||
Oruko | Ìyí Alcoholysis (mol%) | Igi (mPa.s) | Ẹka ti o le yipada (%) | Eeru (%) | PH | Mimo(%) |
086-03 | 85.0-87.0 | 3.4-4.2 | 5 | 0.4 | 5.0-7.0 | 93.5 |
098-05 | 98.0-99.0 | 5.0-6.5 | 5 | 0.5 | 5.0-7.0 | 93.5 |
098-08 | 98.0-99.0 | 9.0-11.0 | 5 | 0.5 | 5.0-7.0 | 93.5 |
092-20 | 91.0-93.0 | 21.0-27.0 | 5 | 0.5 | 5.0-7.0 | 93.5 |
094-27 | 94.0-96.0 | 22.0-28.0 | 5 | 0.5 | 5.0-7.0 | 93.5 |
096-27 | 96.0-98.0 | 23.0-29.0 | 5 | 0.5 | 5.0-7.0 | 93.5 |
100-27 | 99.0-100.0 | 22.0-28.0 | 5 | 0.7 | / | 93.5 |
092-35 | 91.0-93.0 | 30.0-36.0 | 5 | 0.3 | 5.0-7.0 | 93.5 |
100-35 | 99.0-100.0 | 35.0-43.0 | 5 | 0.7 | 5.0-7.0 | 93.5 |
098-60 | 98.0-99.0 | 58.0-68.0 | 5 | 0.5 | 5.0-7.0 | 93.5 |
100-60 | 99.0-100.0 | 58.0-68.0 | 5 | 0.7 | 5.0-7.0 | 93.5 |
098-70 | 99.0-100.0 | 68.0-78.0 | 5 | 0.7 | 5.0-7.0 | 93.5 |
PVA Sinopec Atọka imuse boṣewa ile-iṣẹ (q/sh1115105) | ||||||
Oruko | Ìyí Alcoholysis (mol%) | Igi (mPa.s) | Ẹka ti o le yipada (%) | Eeru (%) | PH | Mimo(%) |
100-27S | 99.5-100 | 23.0-29.0 | 6.0 | 0.8 | - | 92.0 |
100-40 | 99.5-100 | 35.0-45.0 | 6.0 | 0.8 | - | 92.0 |
100-78 | 99.5-100 | 73.0-83.0 | 6.0 | 0.8 | - | 92.0 |
098-03 | 98.0-98.8 | 3.2-4.0 | 5.0 | 0.7 | 5.0-7.0 | 94.0 |
098-04 | 98.0-98.8 | 4.0-5.0 | 5.0 | 0.5 | 5.0-7.0 | 94.0 |
098-10 | 98.0-98.8 | 8.0-12.0 | 5.0 | 0.5 | 5.0-7.0 | 94.0 |
098-15 | 98.0-98.8 | 13.0-17.0 | 5.0 | 0.5 | 5.0-7.0 | 94.0 |
098-20 | 98.0-98.8 | 18.0-22.0 | 5.0 | 0.5 | 5.0-7.0 | 94.0 |
098-27 | 98.0-98.8 | 23.0-29.0 | 5.0 | 0.5 | 5.0-7.0 | 94.0 |
098-30 | 98.0-98.8 | 28.0-32.0 | 5.0 | 0.5 | 5.0-7.0 | 94.0 |
097-29 | 96.0-98.0 | 37.0-31.0 | 5.0 | 0.5 | 5.0-7.0 | 94.0 |
097-60 | 96.0-98.0 | 56.0-66.0 | 5.0 | 0.5 | 5.0-7.0 | 94.0 |
092-53 | 91.0-93.0 | 48.0-58.0 | 5.0 | 0.5 | 5.0-7.0 | 94.0 |
088-03 | 86.5-88.5 | 3.0-4.0 | 5.0 | 0.7 | 5.0-7.0 | 94.0 |
088-05 | 86.5-88.5 | 4.5-6.0 | 5.0 | 0.5 | 5.0-7.0 | 94.0 |
088-08 | 86.5-88.5 | 8.0-10.0 | 5.0 | 0.5 | 5.0-7.0 | 94.0 |
088-13 | 86.5-88.5 | 12.0-14.0 | 5.0 | 0.5 | 5.0-7.0 | 94.0 |
088-20 | 86.5-88.5 | 21.0-24.5 | 5.0 | 0.4 | 5.0-7.0 | 94.0 |
088-26 | 86.5-88.5 | 24.0-28.0 | 5.0 | 0.5 | 5.0-7.0 | 94.0 |
088-35 | 86.5-88.5 | 29.0-34.0 | 5.0 | 0.3 | 5.0-7.0 | 94.0 |
088-40 | 86.5-88.5 | 38.0-42.0 | 5.0 | 0.5 | 5.0-7.0 | 94.0 |
088-50 | 86.5-88.5 | 45.0-55.0 | 5.0 | 0.3 | 5.0-7.0 | 94.0 |
088-60 | 86.5-88.5 | 56.0-66.0 | 5.0 | 0.5 | 5.0-7.0 | 94.0 |
080-44 | 78.0-82.0 | 42.0-52.0 | 5.0 | 0.5 | 5.0-7.0 | 94.0 |
Isọri Iwọn Patiku Ti Awọn ọja Ọti Polyvinyl Powdered
Oruko | G | 60 apapo | 80 apapo | 100 apapo | 120 apapo | |
10 apapo ni ipamọ w% | ≤ 0.5 | - | - | - | - | |
60 apapo ni ipamọ w% | ≥ 95 | - | - | - | ||
80 apapo ni ipamọ w% | - | ≥ 95 | - | ≥ 95 | ||
100 apapo ni ipamọ w% | ≤ 10 | - | - | ≥ 95 | - | |
120 apapo ni ipamọ w% | - | - | - | ≥ 95 |